SAE-AISI 1132 Steel vs. S35135 Stainless Steel

Both SAE-AISI 1132 steel and S35135 stainless steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1132 steel and the bottom bar is S35135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14 to 18
34
Fatigue Strength, MPa 240 to 380
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 400 to 440
390
Tensile Strength: Ultimate (UTS), MPa 640 to 720
590
Tensile Strength: Yield (Proof), MPa 350 to 590
230

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
37
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.4
6.8
Embodied Energy, MJ/kg 19
94
Embodied Water, L/kg 48
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 97
160
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 940
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 25
20
Strength to Weight: Bending, points 21 to 23
19
Thermal Shock Resistance, points 19 to 22
13

Alloy Composition

Carbon (C), % 0.24 to 0.34
0 to 0.080
Chromium (Cr), % 0
20 to 25
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 97.8 to 98.3
28.3 to 45
Manganese (Mn), % 1.4 to 1.7
0 to 1.0
Molybdenum (Mo), % 0
4.0 to 4.8
Nickel (Ni), % 0
30 to 38
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0
0.6 to 1.0
Sulfur (S), % 0.080 to 0.13
0 to 0.015
Titanium (Ti), % 0
0.4 to 1.0