SAE-AISI 1137 Steel vs. ASTM A369 Grade FP21

Both SAE-AISI 1137 steel and ASTM A369 grade FP21 are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is ASTM A369 grade FP21.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 210
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
20
Fatigue Strength, MPa 250 to 400
160
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 430 to 460
300
Tensile Strength: Ultimate (UTS), MPa 700 to 760
470
Tensile Strength: Yield (Proof), MPa 370 to 650
240

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
470
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
4.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 48
61

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
80
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
150
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
17
Strength to Weight: Bending, points 22 to 24
17
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 21 to 23
14

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.050 to 0.15
Chromium (Cr), % 0
2.7 to 3.4
Iron (Fe), % 97.8 to 98.3
94.3 to 96.2
Manganese (Mn), % 1.4 to 1.7
0.3 to 0.6
Molybdenum (Mo), % 0
0.8 to 1.1
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0.080 to 0.13
0 to 0.025