SAE-AISI 1137 Steel vs. EN 1.0426 Steel

Both SAE-AISI 1137 steel and EN 1.0426 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is EN 1.0426 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 210
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
25
Fatigue Strength, MPa 250 to 400
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 430 to 460
330
Tensile Strength: Ultimate (UTS), MPa 700 to 760
520
Tensile Strength: Yield (Proof), MPa 370 to 650
290

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 48
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
230
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
18
Strength to Weight: Bending, points 22 to 24
18
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 21 to 23
16

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.080 to 0.2
Iron (Fe), % 97.8 to 98.3
97.9 to 99.02
Manganese (Mn), % 1.4 to 1.7
0.9 to 1.5
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0.080 to 0.13
0 to 0.015