SAE-AISI 1137 Steel vs. EN 1.0454 Cast Steel

Both SAE-AISI 1137 steel and EN 1.0454 cast steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is EN 1.0454 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
25
Fatigue Strength, MPa 250 to 400
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 700 to 760
550
Tensile Strength: Yield (Proof), MPa 370 to 650
300

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 48
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
19
Strength to Weight: Bending, points 22 to 24
19
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 21 to 23
17

Alloy Composition

Carbon (C), % 0.32 to 0.39
0
Iron (Fe), % 97.8 to 98.3
99.935 to 100
Manganese (Mn), % 1.4 to 1.7
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Sulfur (S), % 0.080 to 0.13
0 to 0.030