SAE-AISI 1137 Steel vs. EN 1.1165 Cast Steel

Both SAE-AISI 1137 steel and EN 1.1165 cast steel are iron alloys. Their average alloy composition is basically identical. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is EN 1.1165 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
11 to 20
Fatigue Strength, MPa 250 to 400
200 to 380
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 700 to 760
600 to 780
Tensile Strength: Yield (Proof), MPa 370 to 650
290 to 620

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 48
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
81 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
230 to 1010
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
21 to 28
Strength to Weight: Bending, points 22 to 24
20 to 24
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 21 to 23
19 to 25

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.25 to 0.32
Iron (Fe), % 97.8 to 98.3
97.2 to 98.6
Manganese (Mn), % 1.4 to 1.7
1.2 to 1.8
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0.080 to 0.13
0 to 0.030

Comparable Variants