SAE-AISI 1137 Steel vs. EN 1.4347 Stainless Steel

Both SAE-AISI 1137 steel and EN 1.4347 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is EN 1.4347 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 17
23
Fatigue Strength, MPa 250 to 400
320
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 700 to 760
660
Tensile Strength: Yield (Proof), MPa 370 to 650
480

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 12
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
16
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.1
Embodied Energy, MJ/kg 19
44
Embodied Water, L/kg 48
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
140
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
570
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 27
24
Strength to Weight: Bending, points 22 to 24
22
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 21 to 23
19

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.050
Chromium (Cr), % 0
25 to 27
Iron (Fe), % 97.8 to 98.3
62.2 to 69.4
Manganese (Mn), % 1.4 to 1.7
0 to 1.5
Nickel (Ni), % 0
5.5 to 7.5
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0 to 1.5
Sulfur (S), % 0.080 to 0.13
0 to 0.020