SAE-AISI 1137 Steel vs. SAE-AISI 1151 Steel

Both SAE-AISI 1137 steel and SAE-AISI 1151 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is SAE-AISI 1151 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 210
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
11 to 17
Fatigue Strength, MPa 250 to 400
260 to 410
Poisson's Ratio 0.29
0.29
Reduction in Area, % 34 to 39
34 to 40
Shear Modulus, GPa 73
72
Shear Strength, MPa 430 to 460
430 to 480
Tensile Strength: Ultimate (UTS), MPa 700 to 760
710 to 800
Tensile Strength: Yield (Proof), MPa 370 to 650
390 to 660

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
10
Electrical Conductivity: Equal Weight (Specific), % IACS 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 48
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
86 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
400 to 1170
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
25 to 28
Strength to Weight: Bending, points 22 to 24
22 to 24
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 21 to 23
22 to 25

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.48 to 0.55
Iron (Fe), % 97.8 to 98.3
98.3 to 98.7
Manganese (Mn), % 1.4 to 1.7
0.7 to 1.0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Sulfur (S), % 0.080 to 0.13
0.080 to 0.13

Comparable Variants