MakeItFrom.com
Menu (ESC)

SAE-AISI 1137 Steel vs. N08535 Stainless Steel

Both SAE-AISI 1137 steel and N08535 stainless steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is N08535 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 17
46
Fatigue Strength, MPa 250 to 400
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Shear Strength, MPa 430 to 460
400
Tensile Strength: Ultimate (UTS), MPa 700 to 760
570
Tensile Strength: Yield (Proof), MPa 370 to 650
240

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
13
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 12
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.4
6.3
Embodied Energy, MJ/kg 19
87
Embodied Water, L/kg 48
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
210
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
20
Strength to Weight: Bending, points 22 to 24
19
Thermal Diffusivity, mm2/s 14
3.3
Thermal Shock Resistance, points 21 to 23
13

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.030
Chromium (Cr), % 0
24 to 27
Copper (Cu), % 0
0 to 1.5
Iron (Fe), % 97.8 to 98.3
29.4 to 44.5
Manganese (Mn), % 1.4 to 1.7
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 4.0
Nickel (Ni), % 0
29 to 36.5
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0.080 to 0.13
0 to 0.030