SAE-AISI 1137 Steel vs. S31277 Stainless Steel

Both SAE-AISI 1137 steel and S31277 stainless steel are iron alloys. They have 42% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is S31277 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 11 to 17
45
Fatigue Strength, MPa 250 to 400
380
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Shear Strength, MPa 430 to 460
600
Tensile Strength: Ultimate (UTS), MPa 700 to 760
860
Tensile Strength: Yield (Proof), MPa 370 to 650
410

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.4
6.7
Embodied Energy, MJ/kg 19
90
Embodied Water, L/kg 48
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
320
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
410
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
29
Strength to Weight: Bending, points 22 to 24
25
Thermal Shock Resistance, points 21 to 23
19

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.020
Chromium (Cr), % 0
20.5 to 23
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 97.8 to 98.3
35.5 to 46.2
Manganese (Mn), % 1.4 to 1.7
0 to 3.0
Molybdenum (Mo), % 0
6.5 to 8.0
Nickel (Ni), % 0
26 to 28
Nitrogen (N), % 0
0.3 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0.080 to 0.13
0 to 0.010