MakeItFrom.com
Menu (ESC)

SAE-AISI 1137 Steel vs. S31655 Stainless Steel

Both SAE-AISI 1137 steel and S31655 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is S31655 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 210
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 17
39
Fatigue Strength, MPa 250 to 400
300
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 430 to 460
490
Tensile Strength: Ultimate (UTS), MPa 700 to 760
710
Tensile Strength: Yield (Proof), MPa 370 to 650
350

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
1010
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 12
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.3
Embodied Energy, MJ/kg 19
46
Embodied Water, L/kg 48
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
230
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 27
25
Strength to Weight: Bending, points 22 to 24
23
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 21 to 23
16

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.030
Chromium (Cr), % 0
19.5 to 21.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 97.8 to 98.3
63.2 to 71.9
Manganese (Mn), % 1.4 to 1.7
0 to 2.0
Molybdenum (Mo), % 0
0.5 to 1.5
Nickel (Ni), % 0
8.0 to 9.5
Nitrogen (N), % 0
0.14 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0.080 to 0.13
0 to 0.015