SAE-AISI 1141 Steel vs. N07041 Nickel
SAE-AISI 1141 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1141 steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 11 to 17 | |
| 14 |
| Fatigue Strength, MPa | 270 to 430 | |
| 540 |
| Shear Strength, MPa | 460 to 480 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 740 to 810 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 400 to 700 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1420 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 51 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 to 110 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 to 1290 | |
| 2510 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 29 | |
| 47 |
| Strength to Weight: Bending, points | 23 to 25 | |
| 34 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.0 |
| Thermal Shock Resistance, points | 24 to 26 | |
| 38 |