SAE-AISI 1141 Steel vs. N08810 Stainless Steel

Both SAE-AISI 1141 steel and N08810 stainless steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1141 steel and the bottom bar is N08810 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 17
33
Fatigue Strength, MPa 270 to 430
160
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Shear Strength, MPa 460 to 480
340
Tensile Strength: Ultimate (UTS), MPa 740 to 810
520
Tensile Strength: Yield (Proof), MPa 400 to 700
200

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
12
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 12
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
5.3
Embodied Energy, MJ/kg 19
76
Embodied Water, L/kg 47
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 86 to 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 430 to 1290
100
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 29
18
Strength to Weight: Bending, points 23 to 25
18
Thermal Diffusivity, mm2/s 14
3.0
Thermal Shock Resistance, points 24 to 26
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0.37 to 0.45
0.050 to 0.1
Chromium (Cr), % 0
19 to 23
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 97.7 to 98.2
39.5 to 50.7
Manganese (Mn), % 1.4 to 1.7
0 to 1.5
Nickel (Ni), % 0
30 to 35
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0.080 to 0.13
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6