SAE-AISI 1151 Steel vs. EN 1.7035 Steel

Both SAE-AISI 1151 steel and EN 1.7035 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1151 steel and the bottom bar is EN 1.7035 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
160 to 290
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 710 to 800
530 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
46
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
19
Embodied Water, L/kg 46
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
19 to 66
Strength to Weight: Bending, points 22 to 24
19 to 43
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 22 to 25
16 to 54

Alloy Composition

Carbon (C), % 0.48 to 0.55
0.38 to 0.45
Chromium (Cr), % 0
0.9 to 1.2
Iron (Fe), % 98.3 to 98.7
97 to 98.1
Manganese (Mn), % 0.7 to 1.0
0.6 to 0.9
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0.080 to 0.13
0 to 0.035