SAE-AISI 1211 Steel vs. EN 2.4669 Nickel

SAE-AISI 1211 steel belongs to the iron alloys classification, while EN 2.4669 nickel belongs to the nickel alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1211 steel and the bottom bar is EN 2.4669 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 29
16
Fatigue Strength, MPa 200 to 280
390
Poisson's Ratio 0.29
0.29
Reduction in Area, % 40 to 50
31
Shear Modulus, GPa 73
73
Shear Strength, MPa 280 to 350
680
Tensile Strength: Ultimate (UTS), MPa 430 to 580
1110
Tensile Strength: Yield (Proof), MPa 260 to 460
720

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
960
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1330
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 52
12
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
60
Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 1.4
10
Embodied Energy, MJ/kg 18
150
Embodied Water, L/kg 46
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 61 to 110
160
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 550
1380
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 15 to 21
37
Strength to Weight: Bending, points 16 to 20
28
Thermal Diffusivity, mm2/s 14
3.1
Thermal Shock Resistance, points 14 to 18
33

Alloy Composition

Aluminum (Al), % 0
0.4 to 1.0
Carbon (C), % 0 to 0.13
0 to 0.080
Chromium (Cr), % 0
14 to 17
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 98.7 to 99.23
5.0 to 9.0
Manganese (Mn), % 0.6 to 0.9
0 to 1.0
Nickel (Ni), % 0
65.9 to 77.7
Niobium (Nb), % 0
0.7 to 1.2
Phosphorus (P), % 0.070 to 0.12
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0.1 to 0.15
0 to 0.015
Titanium (Ti), % 0
2.3 to 2.8