SAE-AISI 1213 Steel vs. EN 1.4305 Stainless Steel

Both SAE-AISI 1213 steel and EN 1.4305 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1213 steel and the bottom bar is EN 1.4305 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 190
200 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 29
14 to 40
Fatigue Strength, MPa 200 to 290
190 to 330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 290 to 360
420 to 550
Tensile Strength: Ultimate (UTS), MPa 440 to 600
610 to 900
Tensile Strength: Yield (Proof), MPa 260 to 470
220 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
930
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
15
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.0
Embodied Energy, MJ/kg 18
42
Embodied Water, L/kg 46
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63 to 110
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 580
120 to 830
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 21
22 to 32
Strength to Weight: Bending, points 17 to 20
20 to 27
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 14 to 19
14 to 20

Alloy Composition

Carbon (C), % 0 to 0.13
0 to 0.1
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 98.4 to 99
66.4 to 74.9
Manganese (Mn), % 0.7 to 1.0
0 to 2.0
Nickel (Ni), % 0
8.0 to 10
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0.070 to 0.12
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0.24 to 0.33
0.15 to 0.35