SAE-AISI 1213 Steel vs. SAE-AISI 4340 Steel
Both SAE-AISI 1213 steel and SAE-AISI 4340 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1213 steel and the bottom bar is SAE-AISI 4340 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 190 | |
| 210 to 360 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 29 | |
| 12 to 22 |
| Fatigue Strength, MPa | 200 to 290 | |
| 330 to 740 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 290 to 360 | |
| 430 to 770 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 600 | |
| 690 to 1280 |
| Tensile Strength: Yield (Proof), MPa | 260 to 470 | |
| 470 to 1150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 430 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 44 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 3.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.7 |
| Embodied Energy, MJ/kg | 18 | |
| 22 |
| Embodied Water, L/kg | 46 | |
| 53 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 to 110 | |
| 79 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 580 | |
| 590 to 3490 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 21 | |
| 24 to 45 |
| Strength to Weight: Bending, points | 17 to 20 | |
| 22 to 33 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 20 to 38 |
Alloy Composition
| Carbon (C), % | 0 to 0.13 | |
| 0.38 to 0.43 |
| Chromium (Cr), % | 0 | |
| 0.7 to 0.9 |
| Iron (Fe), % | 98.4 to 99 | |
| 95.1 to 96.3 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0.6 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.2 to 0.3 |
| Nickel (Ni), % | 0 | |
| 1.7 to 2.0 |
| Phosphorus (P), % | 0.070 to 0.12 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0.24 to 0.33 | |
| 0 to 0.040 |