SAE-AISI 12L14 Steel vs. C79600 Nickel Silver

SAE-AISI 12L14 steel belongs to the iron alloys classification, while C79600 nickel silver belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 12L14 steel and the bottom bar is C79600 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 11 to 25
15
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 72
43
Shear Strength, MPa 280 to 370
290
Tensile Strength: Ultimate (UTS), MPa 440 to 620
480
Tensile Strength: Yield (Proof), MPa 260 to 460
300

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 400
130
Melting Completion (Liquidus), °C 1460
930
Melting Onset (Solidus), °C 1420
880
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 51
36
Thermal Expansion, µm/m-K 12
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
25
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.5
Embodied Energy, MJ/kg 18
57
Embodied Water, L/kg 47
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 64 to 93
63
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 560
400
Stiffness to Weight: Axial, points 13
7.8
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 15 to 22
17
Strength to Weight: Bending, points 16 to 20
17
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 14 to 20
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.15
0
Copper (Cu), % 0
43.5 to 46.5
Iron (Fe), % 97.9 to 98.7
0
Lead (Pb), % 0.15 to 0.35
0.8 to 1.2
Manganese (Mn), % 0.85 to 1.2
1.5 to 2.5
Nickel (Ni), % 0
9.0 to 11
Phosphorus (P), % 0.040 to 0.090
0
Sulfur (S), % 0.26 to 0.35
0
Zinc (Zn), % 0
38.3 to 45.2
Residuals, % 0
0 to 0.5