SAE-AISI 12L14 Steel vs. Zamak 3

SAE-AISI 12L14 steel belongs to the iron alloys classification, while Zamak 3 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 12L14 steel and the bottom bar is Zamak 3.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 170
83
Elastic (Young's, Tensile) Modulus, GPa 190
86
Elongation at Break, % 11 to 25
11
Fatigue Strength, MPa 190 to 290
48
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 72
33
Shear Strength, MPa 280 to 370
210
Tensile Strength: Ultimate (UTS), MPa 440 to 620
280
Tensile Strength: Yield (Proof), MPa 260 to 460
210

Thermal Properties

Latent Heat of Fusion, J/g 250
120
Maximum Temperature: Mechanical, °C 400
95
Melting Completion (Liquidus), °C 1460
390
Melting Onset (Solidus), °C 1420
380
Specific Heat Capacity, J/kg-K 470
410
Thermal Conductivity, W/m-K 51
110
Thermal Expansion, µm/m-K 12
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
38

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
11
Density, g/cm3 7.9
6.4
Embodied Carbon, kg CO2/kg material 1.4
3.0
Embodied Energy, MJ/kg 18
57
Embodied Water, L/kg 47
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 64 to 93
28
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 560
260
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 15 to 22
12
Strength to Weight: Bending, points 16 to 20
15
Thermal Diffusivity, mm2/s 14
43
Thermal Shock Resistance, points 14 to 20
8.6

Alloy Composition

Aluminum (Al), % 0
3.5 to 4.3
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.15
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 97.9 to 98.7
0 to 0.1
Lead (Pb), % 0.15 to 0.35
0 to 0.0050
Magnesium (Mg), % 0
0.020 to 0.060
Manganese (Mn), % 0.85 to 1.2
0
Nickel (Ni), % 0
0 to 0.020
Phosphorus (P), % 0.040 to 0.090
0
Silicon (Si), % 0
0 to 0.030
Sulfur (S), % 0.26 to 0.35
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
95.3 to 96.5