SAE-AISI 1548 Steel vs. SAE-AISI 4340 Steel

Both SAE-AISI 1548 steel and SAE-AISI 4340 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1548 steel and the bottom bar is SAE-AISI 4340 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 250
210 to 360
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 16
12 to 22
Fatigue Strength, MPa 270 to 430
330 to 740
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 440 to 500
430 to 770
Tensile Strength: Ultimate (UTS), MPa 730 to 830
690 to 1280
Tensile Strength: Yield (Proof), MPa 420 to 690
470 to 1150

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
44
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
3.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 19
22
Embodied Water, L/kg 47
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79 to 99
79 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 470 to 1280
590 to 3490
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 30
24 to 45
Strength to Weight: Bending, points 23 to 25
22 to 33
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 23 to 27
20 to 38

Alloy Composition

Carbon (C), % 0.44 to 0.52
0.38 to 0.43
Chromium (Cr), % 0
0.7 to 0.9
Iron (Fe), % 98 to 98.5
95.1 to 96.3
Manganese (Mn), % 1.1 to 1.4
0.6 to 0.8
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0
1.7 to 2.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0 to 0.050
0 to 0.040