SAE-AISI 1552 steel belongs to the iron alloys classification, while AWS BAg-24 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1552 steel and the bottom bar is AWS BAg-24.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
33
Tensile Strength: Ultimate (UTS), MPa 760 to 840
150

Thermal Properties

Latent Heat of Fusion, J/g 250
130
Melting Completion (Liquidus), °C 1460
730
Melting Onset (Solidus), °C 1420
660
Specific Heat Capacity, J/kg-K 470
310
Thermal Expansion, µm/m-K 11
21

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.4
49
Embodied Energy, MJ/kg 19
770

Common Calculations

Stiffness to Weight: Axial, points 13
5.3
Stiffness to Weight: Bending, points 24
16
Strength to Weight: Axial, points 27 to 30
4.6
Strength to Weight: Bending, points 24 to 25
6.9
Thermal Shock Resistance, points 26 to 29
5.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.47 to 0.55
0
Copper (Cu), % 0
19 to 21
Iron (Fe), % 97.9 to 98.3
0
Manganese (Mn), % 1.2 to 1.5
0
Nickel (Ni), % 0
1.5 to 2.5
Phosphorus (P), % 0 to 0.040
0
Silver (Ag), % 0
49 to 51
Sulfur (S), % 0 to 0.050
0
Zinc (Zn), % 0
26 to 30
Residuals, % 0
0 to 0.15