SAE-AISI 1552 steel belongs to the iron alloys classification, while AWS BVAu-7 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1552 steel and the bottom bar is AWS BVAu-7.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
130
Poisson's Ratio 0.29
0.38
Shear Modulus, GPa 72
45
Tensile Strength: Ultimate (UTS), MPa 760 to 840
200

Thermal Properties

Latent Heat of Fusion, J/g 250
140
Melting Completion (Liquidus), °C 1460
1120
Melting Onset (Solidus), °C 1420
1100
Specific Heat Capacity, J/kg-K 470
240
Thermal Expansion, µm/m-K 11
13

Otherwise Unclassified Properties

Density, g/cm3 7.8
15

Common Calculations

Stiffness to Weight: Axial, points 13
4.7
Stiffness to Weight: Bending, points 24
11
Strength to Weight: Axial, points 27 to 30
3.7
Strength to Weight: Bending, points 24 to 25
5.1
Thermal Shock Resistance, points 26 to 29
8.9

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0.47 to 0.55
0 to 0.0050
Cobalt (Co), % 0
0 to 0.060
Gold (Au), % 0
49.5 to 50.5
Iron (Fe), % 97.9 to 98.3
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 1.2 to 1.5
0
Nickel (Ni), % 0
24.5 to 25.5
Palladium (Pd), % 0
23.9 to 26
Phosphorus (P), % 0 to 0.040
0 to 0.0020
Sulfur (S), % 0 to 0.050
0
Zinc (Zn), % 0
0 to 0.0010