SAE-AISI 1552 Steel vs. Class 1 Tungsten
SAE-AISI 1552 steel belongs to the iron alloys classification, while class 1 tungsten belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1552 steel and the bottom bar is class 1 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 250 |
| Elongation at Break, % | 11 to 14 | |
| 5.7 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 98 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 840 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 460 to 650 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 120 |
| Thermal Conductivity, W/m-K | 51 | |
| 21 |
| Thermal Expansion, µm/m-K | 11 | |
| 5.1 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 7.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 22 |
| Embodied Energy, MJ/kg | 19 | |
| 340 |
| Embodied Water, L/kg | 47 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 to 98 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 to 1130 | |
| 660 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 14 |
| Strength to Weight: Axial, points | 27 to 30 | |
| 16 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 14 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 26 to 29 | |
| 48 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.47 to 0.55 | |
| 0 |
| Iron (Fe), % | 97.9 to 98.3 | |
| 0 |
| Manganese (Mn), % | 1.2 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tungsten (W), % | 0 | |
| 90 |
| Residuals, % | 0 | |
| 10 |