SAE-AISI 4130 Steel vs. AISI 316 Stainless Steel

Both SAE-AISI 4130 steel and AISI 316 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4130 steel and the bottom bar is AISI 316 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 300
160 to 360
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13 to 26
8.0 to 55
Fatigue Strength, MPa 320 to 660
210 to 430
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 340 to 640
350 to 690
Tensile Strength: Ultimate (UTS), MPa 530 to 1040
520 to 1180
Tensile Strength: Yield (Proof), MPa 440 to 980
230 to 850

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 420
590
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
3.9
Embodied Energy, MJ/kg 20
53
Embodied Water, L/kg 50
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 180
85 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 2550
130 to 1820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19 to 37
18 to 41
Strength to Weight: Bending, points 19 to 29
18 to 31
Thermal Diffusivity, mm2/s 12
4.1
Thermal Shock Resistance, points 16 to 31
11 to 26

Alloy Composition

Carbon (C), % 0.28 to 0.33
0 to 0.080
Chromium (Cr), % 0.8 to 1.1
16 to 18
Iron (Fe), % 97.3 to 98.2
62 to 72
Manganese (Mn), % 0.4 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.15 to 0.25
2.0 to 3.0
Nickel (Ni), % 0
10 to 14
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 0.75
Sulfur (S), % 0 to 0.040
0 to 0.030