SAE-AISI 4142 Steel vs. EN 1.8503 Steel

Both SAE-AISI 4142 steel and EN 1.8503 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4142 steel and the bottom bar is EN 1.8503 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
300
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
16
Fatigue Strength, MPa 250
600
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 370
610
Tensile Strength: Ultimate (UTS), MPa 590
1000
Tensile Strength: Yield (Proof), MPa 370
910

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
440
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
41
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
3.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.3
Embodied Energy, MJ/kg 20
33
Embodied Water, L/kg 51
57

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
150
Resilience: Unit (Modulus of Resilience), kJ/m3 360
2200
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
35
Strength to Weight: Bending, points 20
28
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 19
29

Alloy Composition

Aluminum (Al), % 0
0 to 0.3
Carbon (C), % 0.4 to 0.45
0.16 to 0.24
Chromium (Cr), % 0.8 to 1.1
1.2 to 1.5
Iron (Fe), % 96.8 to 97.8
95.8 to 97.5
Manganese (Mn), % 0.75 to 1.0
0.4 to 0.8
Molybdenum (Mo), % 0.15 to 0.25
0.65 to 0.8
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.035
Vanadium (V), % 0
0.25 to 0.35