SAE-AISI 4142 Steel vs. S30601 Stainless Steel

Both SAE-AISI 4142 steel and S30601 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 61% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4142 steel and the bottom bar is S30601 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
37
Fatigue Strength, MPa 250
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 370
450
Tensile Strength: Ultimate (UTS), MPa 590
660
Tensile Strength: Yield (Proof), MPa 370
300

Thermal Properties

Latent Heat of Fusion, J/g 250
370
Maximum Temperature: Mechanical, °C 420
950
Melting Completion (Liquidus), °C 1460
1360
Melting Onset (Solidus), °C 1420
1310
Specific Heat Capacity, J/kg-K 470
500
Thermal Expansion, µm/m-K 12
15

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
20
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.5
3.9
Embodied Energy, MJ/kg 20
55
Embodied Water, L/kg 51
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
200
Resilience: Unit (Modulus of Resilience), kJ/m3 360
230
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
22
Thermal Shock Resistance, points 19
16

Alloy Composition

Carbon (C), % 0.4 to 0.45
0 to 0.015
Chromium (Cr), % 0.8 to 1.1
17 to 18
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 96.8 to 97.8
56.9 to 60.5
Manganese (Mn), % 0.75 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 0.15 to 0.25
0 to 0.2
Nickel (Ni), % 0
17 to 18
Nitrogen (N), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
5.0 to 5.6
Sulfur (S), % 0 to 0.040
0 to 0.013