SAE-AISI 4142 Steel vs. S32750 Stainless Steel

Both SAE-AISI 4142 steel and S32750 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 64% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4142 steel and the bottom bar is S32750 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
270
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 20
17
Fatigue Strength, MPa 250
360
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
81
Shear Strength, MPa 370
530
Tensile Strength: Ultimate (UTS), MPa 590
860
Tensile Strength: Yield (Proof), MPa 370
590

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
15
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
21
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
4.1
Embodied Energy, MJ/kg 20
56
Embodied Water, L/kg 51
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
130
Resilience: Unit (Modulus of Resilience), kJ/m3 360
860
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
31
Strength to Weight: Bending, points 20
26
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 19
25

Alloy Composition

Carbon (C), % 0.4 to 0.45
0 to 0.030
Chromium (Cr), % 0.8 to 1.1
24 to 26
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 96.8 to 97.8
58.1 to 66.8
Manganese (Mn), % 0.75 to 1.0
0 to 1.2
Molybdenum (Mo), % 0.15 to 0.25
3.0 to 5.0
Nickel (Ni), % 0
6.0 to 8.0
Nitrogen (N), % 0
0.24 to 0.32
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0 to 0.8
Sulfur (S), % 0 to 0.040
0 to 0.020