SAE-AISI 4718 Steel vs. EN 1.8515 Steel

Both SAE-AISI 4718 steel and EN 1.8515 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4718 steel and the bottom bar is EN 1.8515 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
340
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 24
11
Fatigue Strength, MPa 270
580
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 330
680
Tensile Strength: Ultimate (UTS), MPa 510
1130
Tensile Strength: Yield (Proof), MPa 370
940

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
470
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
40
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
3.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.6
Embodied Energy, MJ/kg 21
22
Embodied Water, L/kg 51
60

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 360
2310
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
40
Strength to Weight: Bending, points 18
31
Thermal Diffusivity, mm2/s 10
11
Thermal Shock Resistance, points 17
33

Alloy Composition

Carbon (C), % 0.16 to 0.21
0.28 to 0.35
Chromium (Cr), % 0.35 to 0.55
2.8 to 3.3
Iron (Fe), % 96.3 to 97.4
94.7 to 96.5
Manganese (Mn), % 0.7 to 0.9
0.4 to 0.7
Molybdenum (Mo), % 0.3 to 0.4
0.3 to 0.5
Nickel (Ni), % 0.9 to 1.2
0 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.035