SAE-AISI 50B50 Steel vs. S30815 Stainless Steel

Both SAE-AISI 50B50 steel and S30815 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 67% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 50B50 steel and the bottom bar is S30815 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
45
Fatigue Strength, MPa 260
320
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 370
480
Tensile Strength: Ultimate (UTS), MPa 590
680
Tensile Strength: Yield (Proof), MPa 370
350

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 410
1020
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1410
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 45
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.3
Embodied Energy, MJ/kg 19
47
Embodied Water, L/kg 48
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
260
Resilience: Unit (Modulus of Resilience), kJ/m3 370
310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
25
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 17
15

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.48 to 0.53
0.050 to 0.1
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 0.4 to 0.6
20 to 22
Iron (Fe), % 97.4 to 98.2
62.8 to 68.4
Manganese (Mn), % 0.75 to 1.0
0 to 0.8
Nickel (Ni), % 0
10 to 12
Nitrogen (N), % 0
0.14 to 0.2
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
1.4 to 2.0
Sulfur (S), % 0 to 0.040
0 to 0.030