SAE-AISI 5120 Steel vs. C19010 Copper

SAE-AISI 5120 steel belongs to the iron alloys classification, while C19010 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5120 steel and the bottom bar is C19010 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 16
2.4 to 22
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
43
Shear Strength, MPa 310
210 to 360
Tensile Strength: Ultimate (UTS), MPa 500
330 to 640
Tensile Strength: Yield (Proof), MPa 320
260 to 620

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Maximum Temperature: Mechanical, °C 420
200
Melting Completion (Liquidus), °C 1460
1060
Melting Onset (Solidus), °C 1420
1010
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 47
260
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
48 to 63
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
48 to 63

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
31
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.4
2.7
Embodied Energy, MJ/kg 19
42
Embodied Water, L/kg 49
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71
7.3 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 280
290 to 1680
Stiffness to Weight: Axial, points 13
7.3
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 18
10 to 20
Strength to Weight: Bending, points 18
12 to 18
Thermal Diffusivity, mm2/s 13
75
Thermal Shock Resistance, points 16
12 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.17 to 0.22
0
Chromium (Cr), % 0.7 to 0.9
0
Copper (Cu), % 0
97.3 to 99.04
Iron (Fe), % 97.6 to 98.3
0
Manganese (Mn), % 0.7 to 0.9
0
Nickel (Ni), % 0
0.8 to 1.8
Phosphorus (P), % 0 to 0.035
0.010 to 0.050
Silicon (Si), % 0.15 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.040
0
Residuals, % 0
0 to 0.5