SAE-AISI 5130 Steel vs. SAE-AISI 1524 Steel

Both SAE-AISI 5130 steel and SAE-AISI 1524 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5130 steel and the bottom bar is SAE-AISI 1524 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 190
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 22
14 to 22
Fatigue Strength, MPa 230 to 330
230 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 310 to 390
360 to 390
Tensile Strength: Ultimate (UTS), MPa 500 to 640
570 to 650
Tensile Strength: Yield (Proof), MPa 330 to 530
320 to 540

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
8.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 50
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 74 to 98
84 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 750
270 to 760
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 23
20 to 23
Strength to Weight: Bending, points 18 to 21
19 to 21
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 16 to 20
18 to 21

Alloy Composition

Carbon (C), % 0.28 to 0.33
0.19 to 0.25
Chromium (Cr), % 0.8 to 1.1
0
Iron (Fe), % 97.2 to 98.1
98 to 98.5
Manganese (Mn), % 0.7 to 0.9
1.4 to 1.7
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.040
0 to 0.050

Comparable Variants