SAE-AISI 5155 Steel vs. 6082 Aluminum

SAE-AISI 5155 steel belongs to the iron alloys classification, while 6082 aluminum belongs to the aluminum alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is SAE-AISI 5155 steel and the bottom bar is 6082 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
40 to 95
Elastic (Young's, Tensile) Modulus, GPa 190
69
Elongation at Break, % 21
6.3 to 18
Fatigue Strength, MPa 260
55 to 130
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Shear Strength, MPa 390
84 to 220
Tensile Strength: Ultimate (UTS), MPa 620
140 to 340
Tensile Strength: Yield (Proof), MPa 380
85 to 320

Thermal Properties

Latent Heat of Fusion, J/g 250
410
Maximum Temperature: Mechanical, °C 420
170
Melting Completion (Liquidus), °C 1450
650
Melting Onset (Solidus), °C 1410
580
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 49
160
Thermal Expansion, µm/m-K 12
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
42
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
140

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.4
8.3
Embodied Energy, MJ/kg 19
150
Embodied Water, L/kg 49
1170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
19 to 43
Resilience: Unit (Modulus of Resilience), kJ/m3 380
52 to 710
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 22
14 to 35
Strength to Weight: Bending, points 21
21 to 40
Thermal Diffusivity, mm2/s 13
67
Thermal Shock Resistance, points 20
6.0 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
95.2 to 98.3
Carbon (C), % 0.51 to 0.59
0
Chromium (Cr), % 0.7 to 0.9
0 to 0.25
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 97.2 to 97.9
0 to 0.5
Magnesium (Mg), % 0
0.6 to 1.2
Manganese (Mn), % 0.7 to 0.9
0.4 to 1.0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0.15 to 0.35
0.7 to 1.3
Sulfur (S), % 0 to 0.040
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0
0 to 0.15