SAE-AISI 51B60 Steel vs. R31233 Cobalt

SAE-AISI 51B60 steel belongs to the iron alloys classification, while R31233 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 51B60 steel and the bottom bar is R31233 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 12 to 21
17
Fatigue Strength, MPa 280 to 340
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
85
Tensile Strength: Ultimate (UTS), MPa 660
1020
Tensile Strength: Yield (Proof), MPa 400 to 550
420

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Melting Completion (Liquidus), °C 1450
1350
Melting Onset (Solidus), °C 1410
1330
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 43
12
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.1

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.4
8.4
Embodied Energy, MJ/kg 19
110
Embodied Water, L/kg 49
480

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 73 to 120
140
Resilience: Unit (Modulus of Resilience), kJ/m3 420 to 800
410
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 23
33
Strength to Weight: Bending, points 22
26
Thermal Diffusivity, mm2/s 12
3.2
Thermal Shock Resistance, points 19
25

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0 to 0.015
Carbon (C), % 0.56 to 0.64
0.020 to 0.1
Chromium (Cr), % 0.7 to 0.9
23.5 to 27.5
Cobalt (Co), % 0
44.7 to 63.3
Iron (Fe), % 97 to 97.8
1.0 to 5.0
Manganese (Mn), % 0.75 to 1.0
0.1 to 1.5
Molybdenum (Mo), % 0
4.0 to 6.0
Nickel (Ni), % 0
7.0 to 11
Nitrogen (N), % 0
0.030 to 0.12
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0.050 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.020
Tungsten (W), % 0
1.0 to 3.0