SAE-AISI 52100 Steel vs. EN 1.7233 Steel

Both SAE-AISI 52100 steel and EN 1.7233 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 52100 steel and the bottom bar is EN 1.7233 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 210
210 to 290
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 10 to 20
18 to 23
Fatigue Strength, MPa 250 to 340
270 to 530
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 370 to 420
450 to 590
Tensile Strength: Ultimate (UTS), MPa 590 to 2010
700 to 960
Tensile Strength: Yield (Proof), MPa 360 to 560
380 to 780

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
430
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 47
39
Thermal Expansion, µm/m-K 12 to 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
3.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.6
Embodied Energy, MJ/kg 20
21
Embodied Water, L/kg 51
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 54 to 310
110 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 350 to 840
380 to 1630
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 72
25 to 34
Strength to Weight: Bending, points 20 to 45
22 to 28
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 19 to 61
21 to 28

Alloy Composition

Carbon (C), % 0.93 to 1.1
0.39 to 0.45
Chromium (Cr), % 1.4 to 1.6
1.2 to 1.5
Iron (Fe), % 96.5 to 97.3
96.2 to 97.5
Manganese (Mn), % 0.25 to 0.45
0.4 to 0.7
Molybdenum (Mo), % 0
0.5 to 0.7
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.035

Comparable Variants