SAE-AISI 8627 Steel vs. ASTM A387 Grade 2 Steel

Both SAE-AISI 8627 steel and ASTM A387 grade 2 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 8627 steel and the bottom bar is ASTM A387 grade 2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
25
Fatigue Strength, MPa 230
190 to 250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 320
300 to 350
Tensile Strength: Ultimate (UTS), MPa 500
470 to 550
Tensile Strength: Yield (Proof), MPa 330
260 to 350

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
420
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 38
45
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
2.6
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.6
Embodied Energy, MJ/kg 20
20
Embodied Water, L/kg 50
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
98 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 280
180 to 320
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
16 to 20
Strength to Weight: Bending, points 18
17 to 19
Thermal Diffusivity, mm2/s 10
12
Thermal Shock Resistance, points 17
14 to 16

Alloy Composition

Carbon (C), % 0.25 to 0.3
0.050 to 0.21
Chromium (Cr), % 0.4 to 0.6
0.5 to 0.8
Iron (Fe), % 96.8 to 98
97.1 to 98.3
Manganese (Mn), % 0.7 to 0.9
0.55 to 0.8
Molybdenum (Mo), % 0.15 to 0.25
0.45 to 0.6
Nickel (Ni), % 0.4 to 0.7
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0.15 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.025