SAE-AISI 8627 Steel vs. EN 1.8932 Steel

Both SAE-AISI 8627 steel and EN 1.8932 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is SAE-AISI 8627 steel and the bottom bar is EN 1.8932 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
20
Fatigue Strength, MPa 230
250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 320
370
Tensile Strength: Ultimate (UTS), MPa 500
600
Tensile Strength: Yield (Proof), MPa 330
370

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 38
40
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.7
Embodied Energy, MJ/kg 20
24
Embodied Water, L/kg 50
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
100
Resilience: Unit (Modulus of Resilience), kJ/m3 280
370
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 10
11
Thermal Shock Resistance, points 17
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Carbon (C), % 0.25 to 0.3
0 to 0.2
Chromium (Cr), % 0.4 to 0.6
0 to 0.3
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 96.8 to 98
95.5 to 98.9
Manganese (Mn), % 0.7 to 0.9
1.0 to 1.7
Molybdenum (Mo), % 0.15 to 0.25
0 to 0.1
Nickel (Ni), % 0.4 to 0.7
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0.1 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.015
Vanadium (V), % 0
0 to 0.2