SAE-AISI 8627 Steel vs. S35135 Stainless Steel

Both SAE-AISI 8627 steel and S35135 stainless steel are iron alloys. Both are furnished in the annealed condition. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 8627 steel and the bottom bar is S35135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
34
Fatigue Strength, MPa 230
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 320
390
Tensile Strength: Ultimate (UTS), MPa 500
590
Tensile Strength: Yield (Proof), MPa 330
230

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 11
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
37
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.5
6.8
Embodied Energy, MJ/kg 20
94
Embodied Water, L/kg 50
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
160
Resilience: Unit (Modulus of Resilience), kJ/m3 280
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 18
19
Thermal Shock Resistance, points 17
13

Alloy Composition

Carbon (C), % 0.25 to 0.3
0 to 0.080
Chromium (Cr), % 0.4 to 0.6
20 to 25
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 96.8 to 98
28.3 to 45
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
4.0 to 4.8
Nickel (Ni), % 0.4 to 0.7
30 to 38
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0.6 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015
Titanium (Ti), % 0
0.4 to 1.0