SAE-AISI 8627 Steel vs. S44735 Stainless Steel

Both SAE-AISI 8627 steel and S44735 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 67% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 8627 steel and the bottom bar is S44735 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
220
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 23
21
Fatigue Strength, MPa 230
300
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
82
Shear Strength, MPa 320
390
Tensile Strength: Ultimate (UTS), MPa 500
630
Tensile Strength: Yield (Proof), MPa 330
460

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 11
11

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
21
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
4.4
Embodied Energy, MJ/kg 20
61
Embodied Water, L/kg 50
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
120
Resilience: Unit (Modulus of Resilience), kJ/m3 280
520
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 18
23
Strength to Weight: Bending, points 18
21
Thermal Shock Resistance, points 17
20

Alloy Composition

Carbon (C), % 0.25 to 0.3
0 to 0.030
Chromium (Cr), % 0.4 to 0.6
28 to 30
Iron (Fe), % 96.8 to 98
60.7 to 68.4
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
3.6 to 4.2
Nickel (Ni), % 0.4 to 0.7
0 to 1.0
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0 to 0.045
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030
Titanium (Ti), % 0
0.2 to 1.0