SAE-AISI 8627 Steel vs. S46910 Stainless Steel

Both SAE-AISI 8627 steel and S46910 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 8627 steel and the bottom bar is S46910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
270 to 630
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
2.2 to 11
Fatigue Strength, MPa 230
250 to 1020
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 320
410 to 1410
Tensile Strength: Ultimate (UTS), MPa 500
680 to 2470
Tensile Strength: Yield (Proof), MPa 330
450 to 2290

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 410
810
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 11
11

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
18
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
4.1
Embodied Energy, MJ/kg 20
55
Embodied Water, L/kg 50
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
48 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 280
510 to 4780
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
24 to 86
Strength to Weight: Bending, points 18
22 to 51
Thermal Shock Resistance, points 17
23 to 84

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.5
Carbon (C), % 0.25 to 0.3
0 to 0.030
Chromium (Cr), % 0.4 to 0.6
11 to 13
Copper (Cu), % 0
1.5 to 3.5
Iron (Fe), % 96.8 to 98
65 to 76
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
3.0 to 5.0
Nickel (Ni), % 0.4 to 0.7
8.0 to 10
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0 to 0.7
Sulfur (S), % 0 to 0.040
0 to 0.015
Titanium (Ti), % 0
0.5 to 1.2