SAE-AISI 8630 Steel vs. ACI-ASTM CA15M Steel
Both SAE-AISI 8630 steel and ACI-ASTM CA15M steel are iron alloys. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 8630 steel and the bottom bar is ACI-ASTM CA15M steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 200 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 24 | |
| 20 |
| Fatigue Strength, MPa | 260 to 350 | |
| 330 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 680 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 360 to 560 | |
| 510 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 760 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 39 | |
| 27 |
| Thermal Expansion, µm/m-K | 11 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 3.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 3.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 7.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.1 |
| Embodied Energy, MJ/kg | 20 | |
| 29 |
| Embodied Water, L/kg | 50 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 110 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 340 to 840 | |
| 670 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 24 | |
| 25 |
| Strength to Weight: Bending, points | 19 to 22 | |
| 22 |
| Thermal Diffusivity, mm2/s | 10 | |
| 7.2 |
| Thermal Shock Resistance, points | 18 to 23 | |
| 25 |
Alloy Composition
| Carbon (C), % | 0.28 to 0.33 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 11.5 to 14 |
| Iron (Fe), % | 96.8 to 97.9 | |
| 82.1 to 88.4 |
| Manganese (Mn), % | 0.7 to 0.9 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0.15 to 1.0 |
| Nickel (Ni), % | 0.4 to 0.7 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.65 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.040 |