SAE-AISI A9 Steel vs. Nickel 333
SAE-AISI A9 steel belongs to the iron alloys classification, while nickel 333 belongs to the nickel alloys. They have a modest 26% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI A9 steel and the bottom bar is nickel 333.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 2030 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 320 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 35 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.9 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 55 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 4.7 | |
| 8.5 |
| Embodied Energy, MJ/kg | 70 | |
| 120 |
| Embodied Water, L/kg | 82 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 28 to 73 | |
| 21 |
| Strength to Weight: Bending, points | 24 to 46 | |
| 19 |
| Thermal Diffusivity, mm2/s | 9.6 | |
| 2.9 |
| Thermal Shock Resistance, points | 25 to 66 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.45 to 0.55 | |
| 0 to 0.1 |
| Chromium (Cr), % | 4.8 to 5.5 | |
| 24 to 27 |
| Cobalt (Co), % | 0 | |
| 2.5 to 4.0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 87 to 90.5 | |
| 9.3 to 24.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 1.3 to 1.8 | |
| 2.5 to 4.0 |
| Nickel (Ni), % | 1.3 to 1.8 | |
| 44 to 48 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 1.0 to 1.2 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 2.5 to 4.0 |
| Vanadium (V), % | 0.8 to 1.4 | |
| 0 |