SAE-AISI D4 Steel vs. Solder Alloy 714
SAE-AISI D4 steel belongs to the iron alloys classification, while solder alloy 714 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI D4 steel and the bottom bar is solder alloy 714.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
51 |
Elongation at Break, % | 8.4 to 15 | |
17 |
Poisson's Ratio | 0.28 | |
0.36 |
Shear Modulus, GPa | 74 | |
19 |
Tensile Strength: Ultimate (UTS), MPa | 760 to 2060 | |
52 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
62 |
Melting Completion (Liquidus), °C | 1430 | |
220 |
Melting Onset (Solidus), °C | 1380 | |
220 |
Specific Heat Capacity, J/kg-K | 480 | |
220 |
Thermal Conductivity, W/m-K | 31 | |
62 |
Thermal Expansion, µm/m-K | 12 | |
22 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 4.2 | |
13 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 5.0 | |
16 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.7 | |
7.4 |
Embodied Carbon, kg CO2/kg material | 3.3 | |
18 |
Embodied Energy, MJ/kg | 49 | |
300 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
3.8 |
Stiffness to Weight: Bending, points | 25 | |
17 |
Strength to Weight: Axial, points | 27 to 75 | |
1.9 |
Strength to Weight: Bending, points | 24 to 47 | |
4.2 |
Thermal Diffusivity, mm2/s | 8.3 | |
37 |
Thermal Shock Resistance, points | 23 to 63 | |
3.3 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.0010 |
Antimony (Sb), % | 0 | |
0 to 0.1 |
Arsenic (As), % | 0 | |
0 to 0.030 |
Bismuth (Bi), % | 0 | |
0 to 0.1 |
Cadmium (Cd), % | 0 | |
0 to 0.0020 |
Carbon (C), % | 2.1 to 2.4 | |
0 |
Chromium (Cr), % | 11 to 13 | |
0 |
Copper (Cu), % | 0 to 0.25 | |
0.3 to 0.7 |
Gold (Au), % | 0 | |
0 to 0.050 |
Indium (In), % | 0 | |
0 to 0.1 |
Iron (Fe), % | 80.6 to 86.3 | |
0 to 0.020 |
Lead (Pb), % | 0 | |
0 to 0.070 |
Manganese (Mn), % | 0 to 0.6 | |
0 |
Molybdenum (Mo), % | 0.7 to 1.2 | |
0 |
Nickel (Ni), % | 0 to 0.3 | |
0 to 0.010 |
Phosphorus (P), % | 0 to 0.030 | |
0 |
Silicon (Si), % | 0 to 0.6 | |
0 |
Silver (Ag), % | 0 | |
3.8 to 4.2 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Tin (Sn), % | 0 | |
94.6 to 95.9 |
Vanadium (V), % | 0 to 1.0 | |
0 |
Zinc (Zn), % | 0 | |
0 to 0.0010 |