SAE-AISI H12 Steel vs. N07041 Nickel
SAE-AISI H12 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 13 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H12 steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 1850 | |
| 1400 |
Thermal Properties
| Melting Onset (Solidus), °C | 1440 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 36 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 24 to 65 | |
| 47 |
| Strength to Weight: Bending, points | 22 to 42 | |
| 34 |
| Thermal Diffusivity, mm2/s | 9.8 | |
| 3.0 |
| Thermal Shock Resistance, points | 22 to 60 | |
| 38 |