SAE-AISI H13 Steel vs. AISI 310MoLN Stainless Steel

Both SAE-AISI H13 steel and AISI 310MoLN stainless steel are iron alloys. They have 57% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is AISI 310MoLN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
610

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 29
14
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
28
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.3
5.0
Embodied Energy, MJ/kg 64
70
Embodied Water, L/kg 78
200

Common Calculations

PREN (Pitting Resistance) 9.9
34
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25 to 65
21
Strength to Weight: Bending, points 22 to 43
20
Thermal Diffusivity, mm2/s 7.8
3.7
Thermal Shock Resistance, points 25 to 65
14

Alloy Composition

Carbon (C), % 0.32 to 0.45
0 to 0.020
Chromium (Cr), % 4.8 to 5.5
24 to 26
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 88.8 to 92
45.2 to 53.8
Manganese (Mn), % 0.2 to 0.5
0 to 2.0
Molybdenum (Mo), % 1.1 to 1.8
1.6 to 2.6
Nickel (Ni), % 0 to 0.3
20.5 to 23.5
Nitrogen (N), % 0
0.090 to 0.15
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.8 to 1.2
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Vanadium (V), % 0.8 to 1.2
0