SAE-AISI H13 Steel vs. AWS E90C-B3

Both SAE-AISI H13 steel and AWS E90C-B3 are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is AWS E90C-B3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
710

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 29
41
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
4.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.8
Embodied Energy, MJ/kg 64
24
Embodied Water, L/kg 78
59

Common Calculations

PREN (Pitting Resistance) 9.9
5.7
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 65
25
Strength to Weight: Bending, points 22 to 43
23
Thermal Diffusivity, mm2/s 7.8
11
Thermal Shock Resistance, points 25 to 65
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.32 to 0.45
0.050 to 0.12
Chromium (Cr), % 4.8 to 5.5
2.0 to 2.5
Copper (Cu), % 0 to 0.25
0 to 0.35
Iron (Fe), % 88.8 to 92
93.4 to 96.4
Manganese (Mn), % 0.2 to 0.5
0.4 to 1.0
Molybdenum (Mo), % 1.1 to 1.8
0.9 to 1.2
Nickel (Ni), % 0 to 0.3
0 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.8 to 1.2
0.25 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.8 to 1.2
0 to 0.030
Residuals, % 0
0 to 0.5