SAE-AISI H13 Steel vs. EN 1.0599 Steel

Both SAE-AISI H13 steel and EN 1.0599 steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is EN 1.0599 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
620

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 29
47
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.8
Embodied Energy, MJ/kg 64
24
Embodied Water, L/kg 78
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 65
22
Strength to Weight: Bending, points 22 to 43
21
Thermal Diffusivity, mm2/s 7.8
13
Thermal Shock Resistance, points 25 to 65
20

Alloy Composition

Aluminum (Al), % 0
0.010 to 0.050
Carbon (C), % 0.32 to 0.45
0.16 to 0.22
Chromium (Cr), % 4.8 to 5.5
0 to 0.3
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 88.8 to 92
96.1 to 98.4
Manganese (Mn), % 0.2 to 0.5
1.3 to 1.7
Molybdenum (Mo), % 1.1 to 1.8
0 to 0.080
Nickel (Ni), % 0 to 0.3
0 to 0.4
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.8 to 1.2
0.1 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.035
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0.8 to 1.2
0.080 to 0.15