SAE-AISI H13 Steel vs. EN 1.4806 Stainless Steel

Both SAE-AISI H13 steel and EN 1.4806 stainless steel are iron alloys. They have 52% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is EN 1.4806 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
75
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
470

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1340
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 29
12
Thermal Expansion, µm/m-K 10
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
31
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 4.3
5.4
Embodied Energy, MJ/kg 64
76
Embodied Water, L/kg 78
190

Common Calculations

PREN (Pitting Resistance) 9.9
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 65
16
Strength to Weight: Bending, points 22 to 43
17
Thermal Diffusivity, mm2/s 7.8
3.1
Thermal Shock Resistance, points 25 to 65
11

Alloy Composition

Carbon (C), % 0.32 to 0.45
0.3 to 0.5
Chromium (Cr), % 4.8 to 5.5
16 to 18
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 88.8 to 92
40.4 to 48.7
Manganese (Mn), % 0.2 to 0.5
0 to 2.0
Molybdenum (Mo), % 1.1 to 1.8
0 to 0.5
Nickel (Ni), % 0 to 0.3
34 to 36
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.8 to 1.2
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.8 to 1.2
0