SAE-AISI H13 Steel vs. EN 1.7117 Steel

Both SAE-AISI H13 steel and EN 1.7117 steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is EN 1.7117 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
660 to 1930

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 29
43
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
2.6
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
1.5
Embodied Energy, MJ/kg 64
21
Embodied Water, L/kg 78
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25 to 65
24 to 69
Strength to Weight: Bending, points 22 to 43
22 to 44
Thermal Diffusivity, mm2/s 7.8
12
Thermal Shock Resistance, points 25 to 65
20 to 58

Alloy Composition

Carbon (C), % 0.32 to 0.45
0.49 to 0.56
Chromium (Cr), % 4.8 to 5.5
0.7 to 1.0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 88.8 to 92
95.2 to 96.4
Manganese (Mn), % 0.2 to 0.5
0.7 to 1.0
Molybdenum (Mo), % 1.1 to 1.8
0
Nickel (Ni), % 0 to 0.3
0.5 to 0.7
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.8 to 1.2
1.2 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0.8 to 1.2
0

Comparable Variants