SAE-AISI H13 Steel vs. EN 1.7365 Steel

Both SAE-AISI H13 steel and EN 1.7365 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is EN 1.7365 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
74
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
700

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 29
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
4.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.8
Embodied Energy, MJ/kg 64
24
Embodied Water, L/kg 78
70

Common Calculations

PREN (Pitting Resistance) 9.9
6.8
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25 to 65
25
Strength to Weight: Bending, points 22 to 43
22
Thermal Diffusivity, mm2/s 7.8
11
Thermal Shock Resistance, points 25 to 65
20

Alloy Composition

Carbon (C), % 0.32 to 0.45
0.12 to 0.19
Chromium (Cr), % 4.8 to 5.5
4.0 to 6.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 88.8 to 92
91.2 to 94.9
Manganese (Mn), % 0.2 to 0.5
0.5 to 0.8
Molybdenum (Mo), % 1.1 to 1.8
0.45 to 0.65
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.8 to 1.2
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0.8 to 1.2
0 to 0.050