SAE-AISI H13 Steel vs. EN 1.7709 Steel

Both SAE-AISI H13 steel and EN 1.7709 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is EN 1.7709 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
650 to 780

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 29
33
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
3.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
2.3
Embodied Energy, MJ/kg 64
32
Embodied Water, L/kg 78
56

Common Calculations

PREN (Pitting Resistance) 9.9
3.6
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 65
23 to 27
Strength to Weight: Bending, points 22 to 43
21 to 24
Thermal Diffusivity, mm2/s 7.8
8.9
Thermal Shock Resistance, points 25 to 65
22 to 26

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Carbon (C), % 0.32 to 0.45
0.17 to 0.25
Chromium (Cr), % 4.8 to 5.5
1.2 to 1.5
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 88.8 to 92
95.2 to 97.5
Manganese (Mn), % 0.2 to 0.5
0.4 to 0.8
Molybdenum (Mo), % 1.1 to 1.8
0.55 to 0.8
Nickel (Ni), % 0 to 0.3
0 to 0.6
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.8 to 1.2
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.8 to 1.2
0.2 to 0.35