SAE-AISI H13 Steel vs. S32950 Stainless Steel

Both SAE-AISI H13 steel and S32950 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is S32950 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
780

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 29
16
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
3.4
Embodied Energy, MJ/kg 64
47
Embodied Water, L/kg 78
180

Common Calculations

PREN (Pitting Resistance) 9.9
37
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25 to 65
28
Strength to Weight: Bending, points 22 to 43
24
Thermal Diffusivity, mm2/s 7.8
4.3
Thermal Shock Resistance, points 25 to 65
21

Alloy Composition

Carbon (C), % 0.32 to 0.45
0 to 0.030
Chromium (Cr), % 4.8 to 5.5
26 to 29
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 88.8 to 92
60.3 to 69.4
Manganese (Mn), % 0.2 to 0.5
0 to 2.0
Molybdenum (Mo), % 1.1 to 1.8
1.0 to 2.5
Nickel (Ni), % 0 to 0.3
3.5 to 5.2
Nitrogen (N), % 0
0.15 to 0.35
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.8 to 1.2
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.010
Vanadium (V), % 0.8 to 1.2
0